Table C-14. Hydrostatic Test Data for Nominal 1.50-Inch (D;) -2.25-Inch (Dq) 

 Flat Acrylic Windows, Test Specimens 66-70 



(Sealed with grease; radial clearance 0.005 to 0.010 inch; nominal D;/Dq ratio 1.5) 





Specimen Number 



Value 



Parameter 





















66 



67 



68 



69 



70 



Max 



Avg 



Min 



Thickness (in.) 



0.833 



0.838 



0.840 



0.845 



0.857^ 



0.845 



0.839 



0.833 



Dq (actual, in.) 



2.238 



2.238 



2.239 



2.239 



2.238 



2.239 



2.238 



2.238 



Temperature (°F) 



68 



67 



68 



70 



66 



70 



68 



67 



t/D| Ratio (actual) 



0.555 



0.558 



0.560 



0.563 



0.572 



0.572 



0.559 



0.555 



Pressurization Rate (psi/min) 



695 



662 



660 



663 



650 



695 



670 



660 



Pressure (psi) 



Axial D 



isplaceme 



nt of Center Point 



on Windo 



w's Low- 



Pressure F 



ace (in.) 



1,000 



0.001 



0.001 



0.001 



0.001 



0.001 



0.001 



0.001 



0.001 



2,000 



0.002 



0.002 



0.002 



0.002 



0.001 



0.002 



0.002 



0.001 



3,000 



0.002 



0.002 



0.003 



0.002 



0.002 



0.003 



0.002 



0.002 



4,000 



0.006 



0.005 



0.004 



0.003 



0.003 



0.006 



0.004 



0.003 



5,000 



0.012 



0.011 



0.005 



0.003 



0.005 



0.012 



0.008 



0.003 



6,000 



0.016 



0.015 



0.010 



0.004 



0.006 



0.016 



0.011 



0.004 



7,000 



0.021 



0.016 



0.015 



0.011 



0.009 



0.021 



0.016 



0.011 



8,000 



0.025 



0.021 



0.021 



0.015 



0.010 



0.025 



0.020 



0.015 



9,000 



0.030 



0.025 



0.027 



0.020 



0.019 



0.030 



0.026 



0.020 



10,000 



0.034 



0.031 



0.031 



0.026 



0.020 



0.034 



0.031 



0.026 



11,000 



0.039 



0.035 



0.036 



0.031 



0.020 



0.039 



0.035 



0.031 



12,000 



0.044 



0.041 



0.041 



0.035 



0.035 



0.044 



0.040 



0.035 



13,000 



0.050 



0.045 



0.047 



0.040 



0.036 



0.050 



0.045 



0.040 



14,000 



0.056 



0.054 



0.052 



0.047 



0.037 



0.056 



0.052 



0.047 



15,000 



0.063 



0.059 



0.059 



0.053 



0.039 



0.063 



0.059 



0.053 



16,000 



0.070 



0.069 



0.066 



0.064 



0.040 



0.070 



0.067 



0.064 



17,000 



0.078 



0.076 



0.077 



0.072 



0.041 



0.078 



0.076 



0.072 



18,000 



0.091 



0.087 



0.087 



0.083 



0.042 



0.091 



0.087 



0.083 



19,000 



0.103 



0.097 



0.099 



0.096 



0.064 



0.103 



0.099 



0.096 



20,000 



0.119 



0.110 



0.118 



0.111 



0.080 



0.119 



0.115 



0.110 



21,000 



0.144 



0.132 



0.139 



0.137 



i/ 



0.144 



0.138 



0.132 



22,000 



0.180 



0.163 



0.170 



0.183 





0.183 



0.174 



0.163 



23,000 



0.282 



0.232 



0.230 







0.282 



0.248 



0.230 



Displacement at Failure (in.) 





0.325 



0.330 







0.330 



0.328 



0.325 



Pressure at Failure (psi) 



23,100 



23,400 



23,350 



22,800 





23,400 



23,160 



22,800 



\j Abort due to leak at 20,100 psi, not averaged. 



62 