84 Messrs. K. Honda and T. Terada on the 



in strong fields. As for curves (81, H) T>T (dotted lines in 

 figs. 20 and i21) deduced from (I, H) T , T , the general course 

 is quite similar to that of the curves obtained from (SL, r) H , il 

 but quantitatively there is some difference between these 

 two. The difference, however, becomes less with increased 

 tension. 



Nickel. 

 T = H97 gr./mm. 2 ; t = 13°'7 Q. 



7 = 0. 



r=ll'-4. 



r=34'-5; 



r=67'-0. 



s. 



I. 



H. 



I. 



H. 



0-79 

 2-00 

 3-40 

 5-32 

 8-36 

 11-95 

 33-79 

 52-85 

 105-3 

 1710 

 222-5 

 282-8 

 363-2 



I. 



H. 



I. 



0-87 

 1-88 

 4-71 

 7-68 

 1005 

 14-49 

 35-74 

 60-4 

 125-1 

 182-2 

 218-4 

 304-4 

 369-1 



6-5 

 57-0 

 151-7 

 196-0 

 2220 

 262-1 

 3710 

 429-9 

 484-0 

 502-7 

 509-2 

 518-6 

 5220 



0-81 

 1-78 

 307 

 4-99 

 8-11 

 12-48 

 34-12 

 52-7 

 104-1 

 169-1 

 220-4 

 289-9 

 356-9 



61 

 47-4 

 102-0 

 147-1 

 1953 

 248-5 

 360-9 

 406-1 

 463-5 

 491-0 

 501-6 

 503-1 

 512-7 



4-2 



80-5 

 135-3 

 211-7 



273-7 

 302-6 

 368-4 

 398-7 

 448-7 

 478-7 

 491-1 

 500-4 

 507-9 



079 

 1-34 



1-98 

 404 

 8-44 

 13-61 

 33-80 

 52-68 

 104-6 

 169-3 

 220-4 

 2797 

 357-3 



5-0 

 68-8 

 133-2 

 262-6 

 310-5 

 328-8 

 366-2 

 387-7 

 425-7 

 454-2 

 468-0 

 479-1 

 489-1 



T = 3546 gr./mm. 2 ; * = 13°'7 C. 



r-0. 



r = ll'-8. 



r = 34'6. 



r = 66'-9. 



H. 



I. 



H. 



I. 



H. 



I. 



H. 



I. 



0-80 

 201 

 3-80 

 6-55 

 9-73 

 15-03 

 23-30 

 33-86 

 54-1 

 113-6 

 170-7 

 253-7 

 354-0 



4-8 



13-5 



29-9 



595 



91-5 



136-4 



191-4 



2450 



321-3 



4302 



462-6 



483-7 



499-1 



079 

 1-98 

 3-11 

 4-65 

 6-86 

 11-67 

 1751 

 33-48 

 57-28 

 101-8 

 162-3 

 275-8 

 3569 



41 



12-3 



22-1 



37'3 



60-3 



1073 



156-0 



249-7 



322-6 



414-9 



458-9 



487-4 



494-7 



0-80 

 1-77 

 2-98 

 4-53 

 6-98 

 12-08 

 22-53 

 33-68 

 51-85 

 113-3 

 1710 

 252-8 

 353-7 



35 



9-4 

 246 

 57-6 

 123-0 

 195-4 

 250-5 

 287-2 

 332-2 

 418-8 

 454-3 

 479-5 

 493-1 



0-79 

 1-75 



2-84 

 4 06 

 6-52 

 11-22 

 22-08 

 33-15 

 52-87 

 112-3 

 169-3 

 251-6 

 350-5 



2-7 

 14-8 

 1064 

 191-5 

 248-5 

 277-4 

 3106 

 333-9 

 367-3 

 425-6 

 456-5 

 482-2 

 5001 