TABEL II. 
Het quaternaire stelsel : Cu SO4 — Cu CI3 — K3 SO4 — K2 CL — H^O bij 30°. 
Samenstelling der oplossingen in gewichtsprocenten. 
Punt 
Cu SO 4 
Cu CI 3 
K. SO 4 
1 
KCl 
H 3 O 
Vaste phase. 
n 
0.94 
42.45 
0 
7.86 
48.75 
Cu^ + D -)- Di. 2.2 
d 
0 
43.1 
0 
8.4 
48.5 
CUo + D,. 2.2 
n 
0.94 
42.45 
0 
7.86 
48.75 
Cu^ -|- D Dj. 3. 2 
1.59 
42.30 
0 
5.88 
50.23 
Cu^ “1“ D 
m 
3.46 
40.95 
0 
4.34 
51.25 
C 113 CU 5 D 
m 
3.46 
40.95 
0 
4.34 
51.25 
CUi + Cus + D 
b 
2.89 
42.77 
0 
0 
54.34 
Luj + Cus 
3.46 
40.95 
0 
4.34 
51.25 
C 1 I 2 CU 5 -j— D 
4.15 
36.69 
0 
4.79 
54.37 
Cus + D 
Is 
4.48 
34.33 
0 
5.14 
56.05 
5.48 
29.55 
0 
5.74 
59.23 
„ 
1 
7.43 
23.75 
0 
6.26 
62.56 
Cus -j- Di.j.g + D 
4.90 
24.49 
0 
7,64 
62.97 
2.88 
10.71 
0 
18.57 
67.84 
2.29 
10.44 
0 
20.12 
73.15 
2.15 
10.83 
0 
19.97 
67.05 
2.13 
11.38 
0 
19.60 
66.89 
d 
1.75 
11.01 
0 
21.24 
66.00 
1 
1.31 
16.67 
0 
18.54 
63.48 
M 
c 
1.31 
16.57 
0 
18.68 
63.44 
•5 
ca 
0.89 
23.19 
0 
16.38 
59.54 
L 
0.85 
23.73 
0 
16.25 
59.17 
0.66 
21.80 
0 
15.92 
61.62 
1.03 
27.10 
0 
13.70 
58.17 
0.77 
32.57 
0 
12.43 
54.23 
2.03 
27.75 
0 
9.93 
60.29 
1.47 
39.11 
0 
7.17 
52.25 
j 6.06 
19.84 
0 
7.75 
66.35 
Verzad.vlak Di.j.e 